ISO 5002:2013 pdf download.Hot-rolled and cold-reduced electrolytic zinc-coated carbon steel sheet of commercial and drawing qualities.
ISO 5002 specifies the characteristics of carbon steel sheet of commercial and drawing qualities in cut length or coil form, zinc coated by electrolytic deposition. Electrolytic zinc-coated sheet is intended for the manufacture of formed or of miscellaneous parts, and can be supplied chemically treated to render it more suitable for painting. The zinc coating is expressed in micrometres of thickness per side, for equally coated, differentially coated, or one-side-coated sheets. These sheets are generally produced with coatings, which are not intended to withstand outdoor exposure without chemical treatment and painting. Electrolytic zinc-coated sheet can be produced in thicknesses of 036 mm and thicker (normally up to 4,0 mm) and in widths of 600 mm and over in coils or cut lengths. It is recognized that materials thinner than 0,36 mm or thicker than 4,0 mm can be suitable for electrolytic zinc coating, and, if required, be the subject of agreement between the interested parties.
2 Normative references
The following documents, in whole or in part, are normatively referenced in this document and are indispensable for its application. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies.
ISO 6 892-1, Metallic materials — Tensile testing — Part 1: Method of test at room temperature
ISO 7438, Metallic materials — Bend test
ISO 16160, Hot-rolled steel sheet products — Dimensional and shape tolerances
ISO 16162, Cold-rolled steel sheet products — Dimensional and shape tolerances
3 Terms and definitions
For the purposes of this document, the following terms and definitions apply.
3.1
electrolytic zinc-coated steel sheet
product obtained by electrolytic deposition of a zinc coating on steel sheet on a zinc coating line to produce either electrolytic zinc-coated coils or electrolytic zinc-coated cut lengths
3.2
skin pass
light cold rolling of hot-rolled descaled sheet or of the cold-reduced and annealed steel sheet prior to zinc coating
Note I to entry: The purpose of the skin pass is to produce a higher degree of surface smoothness and thereby improve the surface appearance. The skin pass also temporarily minimizes the occurrence of a surface condition known as stretcher strain (Luders lines) or fluting during the fabrication of finished parts. The skin pass also controls and improves flatness. Some increase in hardness and loss of ductility will result from skin passing.
3.3
stabilized interstitial free steel
extra low carbon steel in which all interstitial elements are combined with titanium and/or equivalent elements.ISO 5002 pdf download